BFM-E-1

130-180

1.3-1.8

80-115

1.00-1.44

100-160

1.26-2.01

3.2-6.4

0.40-0.80

BFM-E-2

210-235

2.1-2.35

140-160

1.76-2.01

200-220

2.51-2.76

9.5-10.4

1.19-1.31

"E" symbolize Extrusion

BFM-C-1

130-180

1.3-1.8

80-120

1.00-1.51

100-160

1.26-2.01

4.0-6.4

0.50-0.80

BFM-C-2

180-220

1.8-2.2

100-140

1.26-1.76

120-190

1.51-2.39

6.4-8.0

0.80-1.00

BFM-C-3

210-239

2.1-2.39

140-165

1.76-2.07

150-210

1.88-2.64

8.0-10.4

1.00-1.31

BFM-C-4

240-265

2.4-2.65

156-181

1.96-2.27

200-270

2.51-3.39

10.4-12.5

1.31-1.57

"C" symbolize Calendering

BFM-P-1

140-160

1.4-1.6

88-115

1.10-1.44

100-140

12.6-1.76

3.2-4.8

0.4-0.6

BFM-P-2

240-260

2.4-2.6

160-180

2.01-2.26

170-220

2.14-2.76

10.3-12.7

1.29-1.60

BFM-P-3

285-295

2.85-2.95

180-190

2.26-2.39

220-235

2.76-2.95

15.0-16.8

1.88-2.11

BFM-P-4

245-260

2.45-2.6

170-180

2.14-2.26

210-220

2.64-2.76

11.8-12.8

1.48-1.61

BFM-P-5

260-280

2.6-2.8

180-195

2.26-2.45

240-260

3.01-3.27

13.8-14.8

1.73-1.86

"P" symbolize Plastic Injection

牌号

Grade

弹性力

Extension Strength(MPa)

******承受力Extension
(Mpa)

硬度

Hardness(SHA)

工作温度

Using Temperature(℃)

密度

Density(g/cm3)

BFM-E-1

5-10

30-100

85-98

-10-80

3.6-3.7

BFM-E-2

5-10

40-100

85-98

-10-80

3.6-3.7

"E" symbolize Extrusion

BFM-C-1

7-12

100-200

85-98

-10-80

3.6-3.7

BFM-C-2

7-12

100-300

85-98

-10-80

3.6-3.7

BFM-C-3

7-12

100-200

85-98

-10-60

3.6-3.7

BFM-C-4

7-12

100-300

85-98

-10-80

3.6-3.7

"C" symbolize Calendering

牌号

Grade

熔融指数

Melt Flow Rate
g/10min

密度

Mold Density
g/cm3

挠曲强度

Flexural Strength
MPa

挠曲系数

Flexural modulus
X10-4MPa

收缩率

Percentage Shrinking
%

缓冲力

IZOD Impact Strength
X10-3j/m2

BFM-P

100

3.6-3.8

113.8

1.49

14.7

"P" symbolize Plastic Injection

棒形